Additive manufacturing (AM) allows us to create incredibly complex shapes, which would not be possible using traditional manufacturing techniques. However, objects created using AM have different properties from traditional manufacturing routes, which is sometimes a disadvantage.

Laser additive manufacturing (LAM) uses a laser to fuse together metallic, ceramic or other powders into complex 3D shapes, layer by layer. The cooling rates are extremely rapid, and since they are unlike conventional processes we don’t know the optimal conditions to obtain the best properties, delaying the uptake of LAM in the production of safety-critical engineering structures, such as turbine blades, energy storage and biomedical devices. We need a method to see inside the process of LAM to better understand and optimise the laser-matter interaction and powder consolidation mechanisms.

The LAMPR team at The Diamond Light Source - The LAMPR team at The Diamond Light Source
The Additive Manufacturing Team from the Research Complex at Harwell on the Joint Engineering Environment Processing (JEEP, I12) beamline. The Laser Additive Manufacturing Process Replicator (or LAMPR) is on the right .

Based in the Research Complex at Harwell, a team of researchers have worked with scientists at I12, the Joint Engineering Environment Processing (JEEP) beamline and the Central Laser Facility to build a laser additive manufacturing machine which operates on a beamline, allowing you to see into the heart of the process, revealing the underlying physical phenomena during LAM.

Professor Peter Lee, The University of Manchester, MAPP X1 theme lead, who leads the project explains: “The LAM process is very fast, taking place in milliseconds, and to investigate we need microsecond resolution, which can only be achieved with the brilliance of a synchrotron. It allows us to follow the process from powder, through melting and then solidification back into the final solid shape. On JEEP we are investigating the superalloys used in aeroengines, and we need the high energy, hard X-rays produced there  to see inside them.”

For this research, the team created a novel LAM process replicator, the LAMPR, which allows them to image and quantify the formation of the melt track as the layers are printed during AM.

The LAMPR was designed to fit on the beamline and mimics a commercial LAM system, with windows that are transparent to X-rays, allowing scientists to see right into the heart of the LAM process as it takes place. They used X-ray radiography with high temporal and spatial resolution to uncover key mechanisms of laser-matter interaction and powder consolidation during LAM, including the formation and evolution of melt tracks, spatter patterns, the denuded zone (a powder-free zone) and porosity in the deposited layers. The time-resolved quantification of the pore and spatter movements gave crucial information of their flow velocities and direction, which are not possible to acquire using other techniques.

“The LAMPR is a unique piece of equipment, and beamline support was utterly essential. We worked with Diamond staff right from formulating the proposal. Diamond helped with the mechanical design, and the optics and integrating the LAMPR into the control systems”, says Dr Alex Leung, the MAPP PDRA leading the experiments. 

DLSAM_Track_and_pool_forming1.jpg - Figure 2: Using I12 and the LAMPR the complete process of track formation during 3D printing is revealed. A first complete track and details on the laser/gas flow are shown at the top. The first stages of the formation of this track are shown below for the first few milliseconds of track formation.
Leung ACL et al Nature Communications, 2018 9, 1355. A first complete track and details on the laser/gas flow are shown at the top. The first stages of the formation of this track are shown for the first few milliseconds of track formation.

The results of these experiments clarify aspects of the physics underlying LAM, which are crucial for its development. The previous hypothesis was that the formation of surface porosity on finished objects was due to incomplete melting or insufficient liquid feeding. However, this research shows that it is formed via a pore-bursting mechanism. Pores near the surface escape into the atmosphere, leaving behind a surface depression.

Further, the team’s results reveal that the continuous track of melted material often occurs via pre-melting ahead of the main track, driven by surface tension (Marangoni flow), before merging into the main track. Metal vapour and heating of inert gas is a potential source of defects, forming a plume which ejects powder and molten droplets away from the main track. 
By enabling varying process conditions to be studied, the LAMPR allowed the team to create a process map which illustrates how to tune the LAM process to produce a quality product with minimal trial and error. Unlike a traditional process map, synchrotron imaging produces a mechanism map, which reveals the fundamental physics limiting the process window. This enables the alloy, conditions or even process to be altered to overcome the restrictions and obtain a more efficient processing environment.
This methodology sheds new light on the mechanisms of pore formation, including the migration, dissolution, dispersion, and bursting of pores during LAM, and future investigations in these areas will deepen our fundamental understanding of the nature of the laser-matter interaction.

Related publication:
Leung ACL et al. In situ X-ray imaging of defect and molten pool dynamics in laser additive manufacturing. Nature Communications (2018). DOI: 10.1038/s41467-018-03734-7.

This article originally appeared on the Diamond Light Source website and is used here with permission.